Comparison of Beralcast® Alloys to Commonly Used
Materials
(NOTE: All properties listed are typical (or average), ambient
temperature (68F to 77F (20C to 25C)) values unless specified
otherwise |
Property Description |
Units |
Beralcast® |
A356-T6 Al |
AZ91 Mg |
Ti-6Al-4V (Cast) |
6061 T6 Al |
Be S200F |
AlBeMet HIPd AM162H |
363 |
191 |
310 |
Density: |
g/cm3 @ 25ºC
lbs/in3 @ 77ºF |
2.16
0.078 |
2.16
0.078 |
2.16
0.078 |
2.69
0.097 |
1.81
0.066 |
4.43
0.160 |
2.70
0.098 |
1.85
0.067 |
2.10
0.076 |
Melting Point (Liquidus): |
ºC
ºF |
645
1193 |
645
1193 |
645
1193 |
615
1135 |
595
1005 |
1660
3020 |
652
1206 |
1185
2345 |
1082
1980 |
Coefficient of Thermal Expansion: |
mm/m (ppm) @ 25ºC
min/in (ppm) @ 77ºF |
14.2
7.9 |
13.4
7.4 |
Longitudinal
13.2
7.3 |
21.5
11.9 |
26.0
14.0 |
9.0
5.0 |
23.6
13.2 |
11.4
6.3 |
13.9
7.7 |
Specific Heat: |
J/kg-ºK @ 20ºC
Btu/lb-ºF@ 68ºF |
1549.1
0.37 |
1423.5
0.34 |
Similar To
191 |
963.0
0.23 |
1046.7
0.25 |
597.0
0.14 |
896.0
0.21 |
1925.0
0.46 |
1506.0
0.36 |
Thermal Conductivity: |
W/m-ºK @ 25ºC
Btu/h-ft-ºF @ 77ºF |
105.5
61.0 |
180.0
104.0 |
Longitudinal
Similar To
191 |
152.3
88.0 |
72.7
42.0 |
7.8
4.5 |
167.0
96.5 |
216.3
125.0 |
210.0
121.0 |
Modulus of Elasticity in Tension: |
Gpa @ 25ºC
mpsi @ 77ºF |
202.0
29.3 |
202.0
29.3 |
202.0
29.3 |
72.4
10.5 |
44.8
6.5 |
110.0
16.0 |
68.3
10.0 |
303.4
44.0 |
192.0
28.0 |
Specific Stiffness (Modulus/Density): |
Gpa-cm3/g @ 25ºC
Mpsi-in2/Lbs @ 77ºF |
93.5
375.6 |
93.5
375.6 |
93.5
375.6 |
26.9
108.2 |
24.8
98.5 |
24.8
100.0 |
25.3
102.0 |
164.0
656.7 |
-
- |
Poissons Ratio: |
|
0.20 |
0.20 |
- |
0.33 |
0.35 |
0.33 |
0.33 |
0.18 |
0.14 |
Yield Strength: |
Mpa @ 25ºC
ksi @ 77ºF |
289.6
31.0 |
137.9
20.0 |
325.4
47.2 |
206.8
30.0 |
151.7
22.0 |
890.0
129.0 |
275.8
40.0 |
241.3
35.0 |
192.0
28.0 |
Ultimate Tensile Strength: |
Mpa @ 25ºC
ksi @ 77ºF |
289.6
42.0 |
196.5
28.5 |
426.1
61.8 |
275.8
40.0 |
227.5
33.0 |
1035.0
150.0 |
310.3
45.0 |
-
- |
-
- |
Specific Strength: (UTS/Density) |
Mpa-cm3/g @ 25ºC
Ksi-in2/Lbs @ 77ºF |
134.1
538.5 |
91.0
365.4 |
197.3
792.3 |
102.5
412.4 |
125.7
500.0 |
233.6
937.5 |
114.9
459.2 |
-
- |
-
- |
Elongation: 2.54 cm (1 in) Gage: |
% @ 25ºC
% @ 77ºF |
3.0
3.0 |
1.7
1.7 |
Longitudinal
13.2
13.2 |
3.0
3.0 |
3.0
3.0 |
10.0
10.0 |
17.0
17.0 |
-
- |
-
- |
Axial Fatigue: (R=-1.0) |
Mpa @ 25ºC
ksi @ 77ºF |
1 X 10^7
117.2
17.0 |
1 X 10^7
-
- |
1 X 10^7
220.6
32.0 |
1 X 10^7
144.8
21.0 |
1 X 10^7
137.9
20.0 |
-
- |
1 X 10^7
96.5
14.0 |
-
- |
-
- |
Compressive Yield Strength: |
Mpa @ 25ºC
ksi @ 77ºF |
226.1
32.8 |
-
- |
318.5
46.2 |
206.8
30.0 |
165.5
24.0 |
283.0
41.0 |
48.3
7.0 |
207.0
30.0 |
-
- |
Pin Double Shear Strength: |
Mpa @ 25ºC
ksi @ 77ºF |
247.5
35.9 |
-
- |
299.9
43.5 |
193.1
28.0 |
137.9
20.0 |
310.0
45.0 |
206.9
30.0 |
-
- |
-
- |
Pin Type Bearing Yield Strength: (e/D=2.0) |
Mpa @ 25ºC
ksi @ 77ºF |
476.4
69.1 |
-
- |
566.1
82.1 |
386.1
56.0 |
275.8
40.0 |
-
- |
-
- |
-
- |
-
- |
Electrical Conductivity: |
%IACS |
40.0 |
42.0 |
Similar To
191 |
41.0 |
11.0 |
41.0 |
43.0 |
41.0 |
45.0 |
NOTE: a dash (-) indicates that property data was not available
at the time the matrix was generated |